今天給大家分享的是2015年5月份《RSC Advances 》上發(fā)表的一篇名為：Synthesis of magnetic porous γ-Fe₂O₃/C@HKUST-1 composites for efficient removal of dyes and heavy metal ions from aqueous solution

文章摘要如下：

A novel and inexpensive approach was adopted to develop magnetic porous γ-Fe₂O₃/C@HKUST-1 composites for the adsorption of dyes and heavy metal ions from aqueous solution. The γ-Fe₂O₃/C with unique functional groups present such as –OH and –NH₂ was used as the support to directly grow HKUST-1 by a stepwise liquid-phase epitaxy process. The crystallographic, morphology, and magnetic properties as well as porosity of the as-synthesized γ-Fe₂O₃/C @HKUST-1 composites were carefully studied by XRD, SEM, TEM, XPS, TGA, and BET. The results indicated that the BET surface area, micropore volume, and saturation magnetization of the γ-Fe₂O₃/C @HKUST-1 are 993.4 m² g^?1, 0.69 cm³ g^?1, and 12.6 emu g^?1, respectively. In addition, a uniform distribution of ultrafine γ-Fe₂O₃ nanoparticles with an average diameter of 2–3 nm was observed in the γ-Fe₂O₃/C@HKUST-1 composites. Our results showed that methylene blue (MB) and Cr(VI) (used as a model for typical dye pollutants and heavy metal ions) are effectively removed from aqueous solutions by γ-Fe₂O₃/C@HKUST-1. The maximum adsorption capacities were 370.2 and 101.4 mg g^?1 of adsorbent for MB and Cr(VI), respectively. Moreover, a removal efficiency of about 90% was retained after five cycles of consecutive adsorption–desorption. The adsorption kinetics data were well described by a pseudo-second-order model (R² > 0.99), and equilibrium data were well fitted to the Langmuir isotherm model (R² > 0.99). Finally, our results suggested that the γ-Fe₂O₃/C@HKUST-1 composites have a great potential to be employed for treatment of wastewater containing MB and Cr(VI).